| 1. | The effect of composition of coating solution , dipping time and other technical parameters for preparation of sensors on sensing behaviour has also been described and discussed
讨论了溶液组成，浸渍时间等元件制备工艺参数对响应特性的影响。发现电极结构对于元件响应特性有一定影响。 |
| 2. | Different factors influencing the effect of antibiosis finishing for knitted socks are experimented ; including concentration of finishing agent , dipping temperature , dipping time , baking temperature , baking time and bath ratio
摘要通过实验确定整理剂浓度、浴比、浸渍温度、浸渍时间、焙烘温度和焙烘时间对涤棉针织袜抗菌防臭整理效果的影响。 |
| 3. | Abstract : in this paper , the preparation of the catalysts for the oxidation of fluorene to fluoreone is studied . the influences of the dipping time , calcining temperature , calcining time and the air quantity during the calcination are discussed
文摘:研究了用工业芴气相氧化制取芴酮的催化剂制作条件，考察了浸渍时间、煅烧温度、煅烧时间和煅烧空气量对催化剂制作的影响 |
| 4. | The compositions and the configurations of the composite films were tested by means of ft - ir , xps and afm . the optimal procedure was obtained by studying the influences of the dipping time , and the annealing temperature on the capacitance increase percentage
借助于ft - ir 、 xps 、 afm等分析手段对复合氧化膜的成分和结构进行了分析,并研究了sol - gel技术的主要工艺参数对铝阳极氧化膜电性能的影响。 |
| 5. | The results show that , the capacitance of aluminum foils is increased at the different rated formation voltage , the forming time become so little that the power was mostly saved , but the withstanding voltages of the dipping foils become lower . the dipping time and the annealing temperature are the key factors influencing the capacitance of aluminum foils fabricated by sol - gel technology . 2
结果表明: sol - gel技术在铝腐蚀箔表面成功制备出了高介电常数的al - ti复合氧化膜;经tio2溶胶处理过的铝腐蚀箔阳极氧化后,复合氧化膜使不同阳极氧化电压下的化成箔比容均有不同程度的提高,而且阳极氧化过程变短,节约了电能;但是耐电压特性变差。 |
| 6. | The oxidizing kinetics equations of different dipping time of dipping two kinds of phosphate saturable solution were determined . the influences of dipping time of dipping two kinds of phosphate saturable solution on antioxygen properties of sic kiln furniture were also studied . the effect of dipping two kinds of phosphate saturable solution were compared . both of their best dipping time were determined
探讨浸渍两种磷酸盐饱和溶液次数对窑具材料结构和性能的影响，确定浸渍两种磷酸盐饱和溶液不同次数的氧化动力学方程，分析其对sic窑具材料抗氧化性的影响，比较两种磷酸盐饱和溶液的浸渍效果，并确定各自的最佳浸渍次数。 |
| 7. | ( 2 ) two methods including one - step and two - step methods were used to modify the platinum electrode . in the two - step method , the experiment conditions were confirmed , namely after modified by nafion film , the electrode was dipped in saturated solution of co ( salen ) for 24h . the electric current would decrease if the dipping time were too long
2 .用两科，方法对电极进行co ( salen ) / nafion修饰，即“一步法”和“两步法” ，对“两步法”的实验条件进行了选择，即将电极表面先修饰好nafion膜后，再浸泡在co ( sa1en )饱和溶液中24h即可，时间再长则峰电流反而会减小。 |
| 8. | X - ray diffraction analysis and mult - peak separation applied software procedure analysis were used to determine the crystal phase and amounts of each sample . the influences of dipping time of dipping two kinds of phosphate saturable solution on the structure and the properties of kiln furniture were studied
探讨浸渍两种磷酸盐饱和溶液的浸渍机理，并用扫描电镜的分析结果加以验证；采用x -射线粉末衍射分析与多峰分离应用软件程序分析、确定各试样的晶相，计算各晶相的含量。 |